New Insights in the Long-Term Atmospheric Corrosion Mechanisms of Low Alloy Steel Reinforcements of Cultural Heritage Buildings

Marie Bouchar (1, 2) , Philippe Dillmann (2, 3) , Delphine D. Neff (2, 3)

1 SGR - Saint-Gobain Recherche
2 LAPA - UMR 3685 - Laboratoire Archéomatériaux et Prévision de l'Altération
3 IRAMAT - LMC - IRAMAT - Laboratoire Métallurgies et Cultures

Reinforcing clamps made of low alloy steel from the Metz cathedral and corroded outdoors during 500 years were studied by OM, FESEM/EDS, and micro-Raman spectroscopy. The corrosion product layer is constituted of a dual structure. The outer layer is mainly constituted of goethite and lepidocrocite embedding exogenous elements such as Ca and P. The inner layer is mainly constituted of ferrihydrite. The behaviour of the inner layer under conditions simulating the wetting stage of the RH wet/dry atmospheric corrosion cycle was observed by in situ micro-Raman spectroscopy. The disappearance of ferrihydrite near the metal/oxide interface strongly suggests a mechanism of reductive dissolution caused by the oxidation of the metallic substrate and was observed for the first time in situ on an archaeological system.

Mots clés: low alloy steel; iron; cultural heritage metals; micro-Raman; in-situ measurement; atmospheric corrosion

Domaines: Matériaux

Marie Bouchar, Philippe Dillmann, Delphine D. Neff. New Insights in the Long-Term Atmospheric Corrosion Mechanisms of Low Alloy Steel Reinforcements of Cultural Heritage Buildings. Materials, 2017, 10, pp.670. ⟨10.3390/ma10060670⟩. ⟨cea-01542525⟩