Intermetallic formation of Al-Fe and Al-Ni phases by ultrafast slurry aluminization (flash aluminizing)

Résumé

Aluminizing of Fe and Ni-based substrates is a conventional process often made by gas phase related techniques (CVD, pack cementation and above the pack), whereby the coating thickness is controlled by solid-state diffusion. Similar coatings can be achieved by slurry aluminizing where self-propagating high temperature synthesis and solid-state diffusion mechanisms are involved. The present work investigates ultrafast (5 min annealing) aluminization to reduce coating time and compares the results on pure iron and nickel substrates with a conventional slurry aluminizing treatment (2 and 5 h). The use of fast heating ramps (25 and 100 °C/min) led to outwardly diffused coatings even with very high Al slurry activities. On nickel, the coatings were homogeneous while on iron, Kirkendall porosity occurred in the outermost layers due to the great dissolution of Fe in the Al melt and its subsequent outward diffusion towards to the Al source.

Domaines

Matériaux
Fichier principal
Vignette du fichier
S0257897220306800.pdf (1.72 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

cea-03303238 , version 1 (22-08-2022)

Licence

Paternité - Pas d'utilisation commerciale

Identifiants

Citer

Thomas Kepa, Fernando Pedraza, Fabien Rouillard. Intermetallic formation of Al-Fe and Al-Ni phases by ultrafast slurry aluminization (flash aluminizing). Surface and Coatings Technology, 2020, 397, pp.126011. ⟨10.1016/j.surfcoat.2020.126011⟩. ⟨cea-03303238⟩
61 Consultations
192 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More