Protection of Low-alloy carbon steel in mildly saline environments by dense ZrO2 coatings

Michel Schlegel 1 Angélique Chabanon 1 Michael Ougier 1 Alexandre Michau 1 Jerome Varlet 1 Hicham Maskrot 1
1 LISL - laboratoire d'ingénierie des surfaces et lasers
SEARS - Service d'études analytiques et de réactivité des surfaces : DEN/DPC/SEARS
Abstract : In the French concept of deep underground nuclear repository, the confinement of high-level nuclear waste is controlled by corrosion of a tight overpack made of low-alloy carbon steel (C-steel). The overpack dimensions are tailored to guarantee confinement during the repository thermal peak, but it may be interesting to increase the overpack lifetime by protective coatings. Due to their physico-chemical properties and corrosion resistance, ceramics such as zirconia (ZrO2) can be used as physical barriers or coatings against interaction between steel surface and corrosive fluids. However, fabrication of oxide coatings has long relied on processes using hazardous or polluting solvents. This limitation can be overcome by techniques such as physical vapor deposition (PVD), which have been spurred by the recent development of High-power impulse magnetron sputtering (HiPIMS). Therefore, the goal of this study was to assess the protective efficiency of C-steel protection against corrosion by PVD-deposited zirconia coatings. A ferrito-perlitic C-steel (P285GH) was were polished, degreased, and used as a substrate in the PVD setup. The steel surfaces were first etched for 10 minutes, and then ZrO2 ceramic coatings were fabricated by reactive PVD-HiPIMS using a zirconium target. The total deposition time, the duration of HiPIMS impulsion, the power density at the target surface and the target-to-substrate distance were varied. Characterization by X-ray diffraction, scanning electron microscopy and Raman microscopy showed that the coatings were homogeneous, relatively dense and composed of monoclinic zirconia forming columns. They were adherent over the entire surface, and displayed only few defects. Variations in the deposition parameters resulted in differences in crystalline properties and coatings thicknesses (between 5 and 10 µm). The corrosion behavior of these coatings in reference (borate buffer) and mildly saline (40 mM NaCl) solutions were assessed in a three-electrode setup (Hg/HgSO4 reference electrode, Pt mesh counter electrode) by monitoring of the open circuit potential (EOCP) and by anodic polarization. Potentials are quoted against the Normal Hydrogen electrode (NHE). The EOCP values measured were generally within ± 0.1 V of the value for bare steel (-0.56 V /NHE), but the corrosion currents were significantly lower, by one to three decades ( ≤ 0.2-5.8×10-8 versus 2.7×10-6 A/cm2, respectively, in 40 mM NaCl). Immersion experiments over three weeks showed that significant variations in the corrosion current occurred, possibly due to corrosion and scaling within coating defects. Overall, however, the corrosion current remained lower than the value measured after one day. These results indicate that dense zirconia coatings may offer interesting protective properties against corrosion in mildly saline environments. Additional experiments over longer timescales, at higher temperatures, and in environmentally representative solutions would aim to further assess the relevancy of such protective coatings.
Document type :
Poster communications
Complete list of metadatas

https://hal-cea.archives-ouvertes.fr/cea-02927607
Contributor : Contributeur Map Cea <>
Submitted on : Tuesday, September 1, 2020 - 6:01:15 PM
Last modification on : Friday, September 4, 2020 - 3:25:15 AM

Identifiers

  • HAL Id : cea-02927607, version 1

Citation

Michel Schlegel, Angélique Chabanon, Michael Ougier, Alexandre Michau, Jerome Varlet, et al.. Protection of Low-alloy carbon steel in mildly saline environments by dense ZrO2 coatings. LTC 2019, Nov 2019, Nancy, France. 2019. ⟨cea-02927607⟩

Share

Metrics

Record views

7