High efficiency fully implanted and co-annealed bifacial n-type solar cells

Résumé

The aim of the study was to develop a very simple process for the fabrication of large area n-type PERT cells by means of ion implantation. We showed an improvement of the implanted boron activation rate with the annealing temperature by comparing boron SIMS and ECV concentration profiles. A direct positive impact on the boron emitter saturation current density (J 0e) was measured. We also investigated the effect of varying the oxidation conditions during the annealing on the implanted boron emitter and the phosphorus BSF quality. Low emitter saturation current density (J 0e) of 131 fA/cm 2 was measured on textured surfaces, close to the value obtained with diffused B-emitters. A process flow was developed leading to an average efficiency of 19% on 239 cm 2 bifacial solar cells, using only eight processing steps with two implantations and one activation annealing.
Fichier principal
Vignette du fichier
Lanterne-2013-Energy procedia-High efficiency fully implanted and co-annealed bifacial n-type solar cells.pdf (632.48 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

cea-02570734 , version 1 (12-05-2020)

Identifiants

Citer

Adeline Lanterne, Samuel Gall, Yannick Veschetti, Raphaël Cabal, Marianne Coig, et al.. High efficiency fully implanted and co-annealed bifacial n-type solar cells. Energy Procedia, 2013, 38, pp.283 - 288. ⟨10.1016/j.egypro.2013.07.279⟩. ⟨cea-02570734⟩
43 Consultations
51 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More