Corrosion monitoring in mixture cement paste - Bentonite

Abstract : Electrochemical Impedance Spectroscopy (EIS) has been used to monitor at the same time the curing process of cement bentonite mixture and the iron corrosion rate in this mixture. It has been shown that the curing process has extended over a period of at least 100 days at room temperature. During this period, the iron corrosion rate was always low i.e. about 2 nm/year in aerated condition and about 1 nm/year in anaerobic condition. These values have confirmed that such cement bentonite mixture was an efficient environment to avoid iron corrosion damages even in aerated condition.
Complete list of metadatas

https://hal-cea.archives-ouvertes.fr/cea-02500833
Contributor : Amplexor Amplexor <>
Submitted on : Friday, March 6, 2020 - 1:25:02 PM
Last modification on : Tuesday, April 28, 2020 - 11:28:17 AM
Long-term archiving on: : Sunday, June 7, 2020 - 2:44:48 PM

Files

201500001626.pdf
Files produced by the author(s)

Identifiers

  • HAL Id : cea-02500833, version 1

Collections

CEA | DEN

Citation

J. Agullo, C. Bataillon, N. Michaud. Corrosion monitoring in mixture cement paste - Bentonite. Global 2015, Sep 2015, Paris, France. ⟨cea-02500833⟩

Share

Metrics

Record views

14

Files downloads

22