In situ TEM annealing of ion-amorphized Hi Nicalon S and Tyranno SA3 SiC fibers

Résumé

In this work, recrystallization of ion-amorphized Hi Nicalon Type S and Tyranno SA3 SiC fibers (4 MeV Au3+, 2 × 1015 cm−2) has been studied via in situ TEM annealing. Both fibers show a two-step recovery process of the radiation damage. First recovery stage starts at temperatures as low as 250 °C and implies recovery of the radiation swelling. Eventually the amorphous layer recrystallizes with no signs of polytype change (3C-SiC). Recrystallization temperatures yield 900–920 °C and 930 °C for the HNS and the TSA3 respectively. HNS fiber shows columnar recrystallization perpendicular to the amorphous–crystalline interphase with a grain growth rate of ∼20 nm min−1. On the other hand, recrystallization of TSA3 fiber is rather “spontaneous” with no preferential growth direction. The different recrystallization is attributed to the different microstructure of the fibers.
Fichier non déposé

Dates et versions

cea-02418713 , version 1 (19-12-2019)

Identifiants

Citer

J. Huguet Garcia, A. Jankowiak, S. Miro, E. Meslin, Y. Serruys, et al.. In situ TEM annealing of ion-amorphized Hi Nicalon S and Tyranno SA3 SiC fibers. Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms, 2016, 374, ⟨10.1016/j.nimb.2015.12.032⟩. ⟨cea-02418713⟩

Collections

CEA DEN
14 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More