# ZnFe$_2$O$_4$ nanoparticles synthesis by laser pyrolysis: interest as new anode material for lithium-ion batteries

1 LEDNA - Laboratoire Edifices Nanométriques
NIMBE UMR 3685 - Nanosciences et Innovation pour les Matériaux, la Biomédecine et l'Energie (ex SIS2M)
Abstract : The development of portable devices, electric vehicles and renewable energies has motivated research works about energy storage for years. Existing lithium-ion batteries cannot reach sufficient energy density to address the needs for such applications. One of the issues limiting the energy density is the low specific capacity of the graphite anode (372 mAh.g$^{-1}$). Mixed-transition metal oxides with a spinel structure (AB$_2$O$_4$$-$A, B transition metals) appear as a promising solution to replace graphite with a higher theoretical capacity (between 750 and 1000 mAh.g$^{-1}$). Nanostructuration of these compounds was studied to maintain mechanical stability and to enhance lithiation kinetics. ZnFe$_2$O$_4$ is an interesting substitute to graphite as the storage mechanism gives rise to a theoretical capacity of 1001 mAh.g$^{-1}$ and among various oxides, ZnFe$_2$O$_4$ is cheap, abundant and non-toxic. Compared with oxides like Fe$_2$O$_3$ , the combination of two transition metals contributes to lower the working voltage vs. Li/Li$^+$ (1.5V for ZnFe$_2$O$_4$ vs. 2.1V for Fe$_2$O$_3$). ZnFe$_2$O$_4$ nanoparticles were synthesized by laser pyrolysis. In this process, an aerosol containing precursors droplets produced by a nebulizer, is flown into the reactor with a carrier gas. In the reactor, a 10.6 $\mu$m-CO$_2$ laser beam decomposes the precursors to obtain nanopowders which are then collected on a filter. The key advantage of laser pyrolysis is the ability to obtain nanomaterials in large scale with a high purity while controlling the grain size with the appropriate parameters. Solutions containing Zn(NO$_3$)$_2$ .6H$_2$O and Fe(NO$_3$)$_3$.9H$_2$O dissolved in deionized water were used for the synthesis of ZnFe$_2$O$_4$ nanoparticles. Ethylene was used as sensitizer gas to absorb the CO$_2$ laser and allow the decomposition of the precursors whereas air and argon were tested as carrier gases. Powders of different morphologies and crystallinities were obtained and characterized by XRD, SEM, EDX, HRTEM and XPS. ZnO and Fe$_2$O$_3$ were also synthesized to compare their electrochemical performances with those of ZnFe$_2$O$_4$. All the results were compared with literature.
Keywords :
Document type :
Conference papers
Domain :
Complete list of metadata

https://hal-cea.archives-ouvertes.fr/cea-02351521
Contributor : Serge Palacin <>
Submitted on : Wednesday, November 6, 2019 - 2:23:31 PM
Last modification on : Friday, March 5, 2021 - 3:04:31 PM
Long-term archiving on: : Saturday, February 8, 2020 - 2:50:22 AM

### File

SMS_Korea2016_abstract_Bourrio...
Files produced by the author(s)

### Identifiers

• HAL Id : cea-02351521, version 1

### Citation

Samantha Bourrioux, Luyuan Wang, Yann Leconte, Madhavi Srinivasan, Zhichuan Xu, et al.. ZnFe$_2$O$_4$ nanoparticles synthesis by laser pyrolysis: interest as new anode material for lithium-ion batteries. 2nd edition Smart Materials and Surfaces, Mar 2016, Incheon, South Korea. ⟨cea-02351521⟩

Record views

Files downloads