The effect of magnesium on the local structure and initial dissolution rate of simplified UK Magnox waste glasses

Abstract : A series of simplified glasses were prepared to mimic the United Kingdom-s Magnox radioactive waste glasses and determine the separate effect of the presence of Mg on the glass structure and the initial dissolution rate. These glasses had an alkaline earth (Ca-Mg) content of 6.5 molpercent and relative ratios of Si, B and Na similar to 25 wtpercent waste loaded Magnox waste glass simulant. Each simplified glass had similar macroscopic properties, differing only in Ca-Mg ratio. 25Mg magic angle spinning nuclear magnetic resonance (MASNMR) spectra of the simplified Mg endmember (MgEM) glass (with no Ca) and the full-component simulant glass were similar, consistent with the similar Mg local environments in both glasses. 11B MASNMR spectra of the series of simplified glasses showed a systematic increase in the amount of three-coordinated boron ((3)B) with increasing amounts of Mg. A clear change in the charge balancing of four-coordinated boron ((4)B) by Mg compared with Ca is observed. However, 11B NMR measurements of the leached material showed that the additional (3)B was not preferentially leached from the Mg containing samples. Despite the structural changes in the glass induced by Ca-Mg substitution, initial dissolution rates (r0) remained invariant, within error, with Ca-Mg ratio. This indicates that the poorer aqueous durability of Mg-containing Magnox waste glass measured experimentally in long-term leaching experiments, compared with SON68 glass containing Ca, is not caused by a primary structural effect in the glass.
Complete list of metadatas

https://hal-cea.archives-ouvertes.fr/cea-02339776
Contributor : Bibliothèque Cadarache <>
Submitted on : Tuesday, November 5, 2019 - 8:44:58 AM
Last modification on : Monday, September 21, 2020 - 11:34:08 AM
Long-term archiving on: : Thursday, February 6, 2020 - 7:43:19 PM

Identifiers

Collections

CEA | DEN

Citation

R. Guo, C.T. Bridgen, S. Gin, S.W. Swanton, I. Farnan. The effect of magnesium on the local structure and initial dissolution rate of simplified UK Magnox waste glasses. Journal of Non-Crystalline Solids, Elsevier, 2018, 497, pp.82-92. ⟨10.1016/j.jnoncrysol.2018.03.002⟩. ⟨cea-02339776⟩

Share

Metrics

Record views

47

Files downloads

111