Interface Analysis of Si-based Anode in Li-ion Batteries through Electrochemical Impedance Spectroscopy and equivalent electrical circuit analysis - CEA - Commissariat à l’énergie atomique et aux énergies alternatives Accéder directement au contenu
Communication Dans Un Congrès Année : 2018

Interface Analysis of Si-based Anode in Li-ion Batteries through Electrochemical Impedance Spectroscopy and equivalent electrical circuit analysis

Résumé

Due to its high capacity compared to graphite, silicon has attracted attention for li-ion battery technology as a promising material for negative electrodes. It is abundant and non-toxic. However: this material is weil known to undergo large volume changes upon lithation and delithation (up to 320 %). This phenomenon causes particle cracking,jnstability of the solid electrolyte interphase (SEI) at the interface between solid Si and liquid electrolyte, and finally leads to electrode delamination and battery performance loss. To overcome these problems, several strategies have been proposed such as using submicronic particles « 150 nm) to mitigate the volume changes and protection of the silicon material with a carbon layer to stabilize the active surface in contact with electrolyte. Combining both strategies, Si@C. core-shell nanoparticles synthesized in one step process have recently been proposed as a promising anode material [1]. Specifically, the Si-based nanoparticles are synthesized in a two stage laser pyrolysis reactor, which yields carbon coated silicon nanoparticles in a si~gle step. This approach mitigates material oxidation because there is no air exposure between the synthesis of the core and shell. Additionally, the nanometric size of the particles prevents material pulverization upon cycling. The synthesis technique also allows control of the core crystallinity, and both highly crystalline and amorphous silicon cores have been synthesized. Moreover, the shell thickness can be tuned by changing the flow of carbon precursor. To optimize the design of composite electrodes based on such active materials, an in-depth understanding of their performance and chemical/mechanical degradation processes remains critical. In this work, the analysis of the electrochemical performances of su ch Si-based electrodes was performed using several electrochemical techniques to compare crystalline or amorphous Si nanoparticles without shell as weil as crystalline Si nanoparticles coated by a thin or a thick layer of carbon (Si@C). The EIS study, carried out at various states of lithiation of Si material, allows tracking the evolution of several critical parameters (for example SEI resistance and charge transfer resistance) of the equivalent electrical circuit describing the elec.trode electrical behavior. Figure la shows typical impedance spectra while Figure lb shows the evolution of the of charge transfer resistance for the different coated and non-coated materials. A very different behavior is observed as a function of the interface material and carbon thickness. The modificatfon of the interface between e1ectrolyte and Si or Si@C materials is also visible on measured equilibrium potentials and power capabilities. This presentation will be devoted to the analysis of the impact of interfaces between electrolyte and Si or Si@C materials on electrochemical performances.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Herlin_ISE2018.pdf (759.39 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

cea-02339691 , version 1 (30-10-2019)

Identifiants

  • HAL Id : cea-02339691 , version 1

Citer

P Bernard, A Desrues, John P. Alper, N. Dufour, C. Haon, et al.. Interface Analysis of Si-based Anode in Li-ion Batteries through Electrochemical Impedance Spectroscopy and equivalent electrical circuit analysis. ISE Topical Meeting, Apr 2018, Tokyo, Japan. ⟨cea-02339691⟩
62 Consultations
36 Téléchargements

Partager

Gmail Facebook X LinkedIn More