Developments in understanding the nucleation of AlN on silicon by MOCVD and its effects on defects - CEA - Commissariat à l’énergie atomique et aux énergies alternatives Accéder directement au contenu
Article Dans Une Revue physica status solidi (a) Année : 2017

Developments in understanding the nucleation of AlN on silicon by MOCVD and its effects on defects

Résumé

We have studied the process of AlN nucleation on silicon by metal-organic chemical vapor phase deposition. We have shown that for our reactor, which incorporates a chlorine-based chamber clean, we require similar growth conditions to those shown to be optimum by molecular beam epitaxy, that is to say a small amount ofNH(3) followed by tri-methyl aluminum(TMAl). When TMAl was introduced first, the resulting layers were low quality and cracked. Furthermore, we have shown that for the highest quality layers, with longer TMAl injection, we have an increased density of "inverted pyramid" defects in the layer which can impact electrical device performance. As we have shown that wafer bow becomes increasingly concave with reduced crystalline quality of the GaN layers, a compromise should be achieved between layer quality and morphology to produce wafers which can be processed into large area, high power transistors. We have been able to produce wafers with a low vertical leakage current density < 100 nAmm(-2) and high breakdown voltage >900V for test structures up to 12mm(2), with a total nitride structure of 3.6 mu m on silicon, resulting in a bow less than <50 mu m on the 200mm wafer.
Fichier non déposé

Dates et versions

cea-02202438 , version 1 (31-07-2019)

Identifiants

Citer

Matthew Charles, Alexis Bavard, Renan Bouis, Yannick Baines, Rene Escoffier. Developments in understanding the nucleation of AlN on silicon by MOCVD and its effects on defects. physica status solidi (a), 2017, 214 (4), pp.1600431. ⟨10.1002/pssa.201600431⟩. ⟨cea-02202438⟩
48 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More