Strong light extraction enhancement using TiO 2 nanoparticles-based microcone arrays embossed on III-Nitride light emitting diodes

Yohan Désières 1, 2, * Ding Yuan Chen 2 Dennis Visser 2 Casper Schippers 2 Srinivasan Anand 2
* Corresponding author
1 KTH - Royal Institute of Technology [Stockholm]
2 CEA-LETI - Laboratoire d'Electronique et des Technologies de l'Information
Abstract : Colloidal TiO2 nanoparticles were used for embossing of composite microcone arrays on III-Nitride vertical-thin-film blue light emitting diodes (LEDs) as well as on silicon, glass, gallium arsenide, and gallium nitride surfaces. Ray tracing simulations were performed to optimize the design of microcones for light extraction and to explain the experimental results. An optical power enhancement of similar to 2.08 was measured on III-Nitride blue LEDs embossed with a hexagonal array of TiO2 microcones of similar to 1.35 mu m in height and similar to 2.6 mu m in base width, without epoxy encapsulation. A voltage increase in similar to 70mV at an operating current density of similar to 35 A/cm(2) was measured for the embossed LEDs. The TiO2 microcone arrays were embossed on functioning LEDs, using low pressures (similar to 100 g/cm(2)) and temperatures <= 100 degrees C.
Document type :
Journal articles
Complete list of metadatas
https://hal-cea.archives-ouvertes.fr/cea-02184488
Contributor : Marianne Leriche <>
Submitted on : Tuesday, July 16, 2019 - 10:07:49 AM
Last modification on : Thursday, July 18, 2019 - 1:27:52 AM

Identifiers

Collections

CEA | DRT | LETI | CEA-GRE

Citation

Yohan Désières, Ding Yuan Chen, Dennis Visser, Casper Schippers, Srinivasan Anand. Strong light extraction enhancement using TiO 2 nanoparticles-based microcone arrays embossed on III-Nitride light emitting diodes. Applied Physics Letters, American Institute of Physics, 2018, 112 (23), pp.231101. ⟨10.1063/1.5021301⟩. ⟨cea-02184488⟩

Export

BibTeX TEI DC DCterms EndNote

Share

Metrics

Record views

10

Contact

support.ccsd.cnrs.fr
hal.support@ccsd.cnrs.fr
Logo CCSD