Diamond delta doped structures exhibiting ultra-sharp interfaces

(1) , (1) , (1) , (1) , (1) , (2)
1
2

Abstract

Boron delta-doping of diamond has appeared as a promising viable approach for the fabrication of high performance RF power transistors taking advantage of diamond properties. Here structures based on p-/p+/p- multilayers were synthesised on (100) HPHT Ib substrates using MPCVD. An original gas injector system was developed enabling to significantly improve the sharpness of both interfaces between p+ and p- layers with a good reproducibility. SIMS profiles recorded on the doping transients still demonstrate an asymmetry of the interface sharpness from 7nm/decade to 2nm/dec on the p-/p+ and the p+/p- interfaces, respectively. The observed differences are here explained and confirmed experimentally, and result from the combination of ion mixing with the effect of the surface roughness, thus limiting the SIMS resolution in depth. The MRI (Mixing Roughness Information) model then allows to evaluate the real value of the delta thickness achievable using this technique to 7 nm and the negative and positive gradients to identical values, namely of 1.4 nm/dec.
Not file

Dates and versions

cea-01901744 , version 1 (23-10-2018)

Identifiers

Cite

C. Mer-Calfati, Nicolas Tranchant, P. Volpe, Jean-Charles Arnault, P. Bergonzo, et al.. Diamond delta doped structures exhibiting ultra-sharp interfaces. 2014 9th European Microwave Integrated Circuits Conference (EuMIC), Oct 2014, Rome, Italy. ⟨10.1109/EuMIC.2014.6997812⟩. ⟨cea-01901744⟩
26 View
0 Download

Altmetric

Share

Gmail Facebook Twitter LinkedIn More