Influence of Electronic Irradiation on Failure and Hardness Properties of Pure Silica Glasses

Résumé

This paper’s focus is the failure and hardness properties of pure amorphous silica (Corning 7980) after β-irradiation at different doses (0-2 GGy). Crack propagation takes place in the SCC regime (10−7-10−10 m.s−1) and Vickers indentation techniques probe the hardness properties of the samples. Irradiation is found to create point defects which mainly include E’ centers, Non-Bridging Oxygen Hole Centers and Peroxy Radicals. β-irradiation herein invokes minor changes in the structure. A small effect of β- irradiation on SCC and hardness variations cannot be eliminated, despite minute variations in the SCC and the hardness properties.

Domaines

Matériaux
Fichier principal
Vignette du fichier
14barletetal14.pdf (369.5 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

cea-01120966 , version 1 (27-02-2015)

Identifiants

Citer

M. Barlet, J-M. Delaye, M. Gennisson, R. Caraballo, B. Boizot, et al.. Influence of Electronic Irradiation on Failure and Hardness Properties of Pure Silica Glasses. 2nd International Summer School on Nuclear Glass Wasteform: Structure, Properties and Long-Term Behavior, SumGLASS 2013, Sep 2013, Pont du Gard, France. pp.286-293, ⟨10.1016/j.mspro.2014.10.037⟩. ⟨cea-01120966⟩
144 Consultations
107 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More